钢号 | C | Si | Mn | P | S | Altot. | Cr | Mo | B | Ti |
max. | max. | max. | max. | max. | min. | max. | max. | max. | max. | |
durostat 400 | 0.18 | 0.60 | 2.10 | 0.025 | 0.010 | 0.020 | 1.00 | 0.50 | 0.005 | 0.050 |
durostat 450 | 0.22 | 0.60 | 2.10 | 0.025 | 0.010 | 0.020 | 1.00 | 0.50 | 0.005 | 0.050 |
durostat 500 | 0.30 | 0.60 | 2.10 | 0.025 | 0.010 | 0.020 | 1.00 | 0.50 | 0.005 | 0.050 |
碳当量 | % | ||||
钢号 |
| CEV 1) | CET 2) | ||
durostat 400 |
| 0.47 | 0.30 | ||
durostat 450 | 0.68 | 0.43 | |||
durostat 500 | 0.53 | 0.41 | |||
2) CET = C + (Mn+Mo)/10 + (Cr+Cu)/20 + Ni/40 according to SEW 088 |
硬度 (保证值) | |||||
钢号 |
| Hardness |
|
|
|
durostat 400 |
| 360 - 440 |
|
|
|
durostat 450 |
| 410 - 490 |
|
|
|
durostat 500 |
| 460 - 540 |
机械性能 (标准值 20mm厚板) | ||||||
钢号 |
| Yield strength |
| Tensile strength |
| Fracture elongation |
|
|
| L0 = 5,65 √ S0 | |||
| Mpa |
| Mpa |
| % | |
durostat 400 |
| 1000 |
| 1250 |
| 10 |
durostat 450 |
| 1100 |
| 1400 |
| 9 |
durostat 500 |
| 1200 |
| 1550 |
| 8 |
尺寸范围 | ||||||
钢号 |
| 厚度 |
| 最大宽度 |
| 最大长度 |
|
|
| ||||
| mm |
| mm |
| mm | |
durostat 400 |
| 8 ≤ 100 |
| 2500 |
| 12750 |
durostat 450 |
| 8 ≤ 30 |
| 2500 |
| 12750 |
durostat 500 |
| 10 ≤ 30 |
| 2500 |
| 12750 |
每张板最大重量 11.7吨 |